Chlorosulfonated polyethylene topcoat (two-pack)
Product Features:
Fast drying; high hardness; strong adhesion, good mechanical properties; excellent protection performance, excellent three-proof performance; good matching performance.
Performance parameters:
1. Color and appearance: the color tone is variable, the paint film is smooth and smooth
2. Non-volatile matter: ≥23%
3. Specific gravity: about 1.22kg/L
4. Drying time: surface dry ≤0.5 hours; hard dry ≤24 hours (under 25℃)
5. Adhesion (circle method): ≤Level 1
6. Flexibility: ≤1mm
7. Impact strength: 50kg•cm
8. Salt water resistance (3%NaCl, 4d): no blistering, no rusting, no falling off, slight discoloration is allowed
9. The composite coating is resistant to 30% NaOH (30d): no bubbles, no rust, no peeling
10. The composite coating is resistant to 30% H2SO4 (30d); no blistering, no rust, no peeling
11. The composite coating is resistant to 30% NaCl (30d); no blistering, no rusting, no peeling
Construction Instructions:
1. Surface treatment: the previous paint film is completely dry, and the oil stains on the paint film are removed.
2. Substrate temperature: 3°C higher than the dew point.
3. Coating method: brush, roller and spray.
4. Thinner: The special thinner for chlorosulfonated polyethylene paint is adjusted to the appropriate viscosity for use.
5. Coating thickness: Generally, it is advisable to coat twice, and the dry film thickness is 50um.
6. Theoretical dosage: about 5.2㎡/kg, (calculated as dry film 30um).
7. Overcoating interval: 6 hours at 25℃, the longest is unlimited.
8. The supporting paint for the front road: chlorosulfonated polyethylene primer.
Security:
1. The construction site should have good ventilation facilities.
2. Construction workers should wear masks, glasses, gloves and other protective equipment to avoid skin contact and inhalation of paint mist and solvents.
3. Smoking is strictly prohibited at the construction site, and all sources of ignition are isolated.